Ashour, T., Derbala, A. (2009). SHRINKAGE OF NATURAL PLASTERING FOR STRAW BUILDINGS AFFECTED BY REINFORCEMENT AND DRYING. test, 26(2), 993-1005. doi: 10.21608/mjae.2009.109764
T. Ashour; A. Derbala. "SHRINKAGE OF NATURAL PLASTERING FOR STRAW BUILDINGS AFFECTED BY REINFORCEMENT AND DRYING". test, 26, 2, 2009, 993-1005. doi: 10.21608/mjae.2009.109764
Ashour, T., Derbala, A. (2009). 'SHRINKAGE OF NATURAL PLASTERING FOR STRAW BUILDINGS AFFECTED BY REINFORCEMENT AND DRYING', test, 26(2), pp. 993-1005. doi: 10.21608/mjae.2009.109764
Ashour, T., Derbala, A. SHRINKAGE OF NATURAL PLASTERING FOR STRAW BUILDINGS AFFECTED BY REINFORCEMENT AND DRYING. test, 2009; 26(2): 993-1005. doi: 10.21608/mjae.2009.109764

SHRINKAGE OF NATURAL PLASTERING FOR STRAW BUILDINGS AFFECTED BY REINFORCEMENT AND DRYING

Misr Journal of Agricultural Engineering
Article 25, Volume 26, Issue 2, April 2009, Pages 993-1005    PDF (308.06 K)
Document Type: Original Article
DOI: 10.21608/mjae.2009.109764
Authors
T. Ashour1; A. Derbala2
1Lect. of Agric. Eng. Dept., Fac. Agric., Moshtohor, Benha Univ., Egypt.
2Lect. of Agric. Eng. Dept., Fac. Agric., Tanta Univ., Egypt.
Abstract
This study was carried out to determine the shrinkage percentage of natural plaster materials consisted of soil, sand and different fibres. The experiments were carried out at the Institute of Production Engineering and Buildings Research, Federal Agricultural Research Center (FAL), Braunschweig, Germany in summer 2007. Straw was used as a reinforcement fiber for plaster and three types of fibers. The plaster materials were put under drying temperatures of 30, 50 and 70 °C.
The results revealed that the highest shrinkage was for plaster reinforced by wood shaving fibres, while the lowest shrinkage was for plaster reinforced by barley straw fibres for treatments A, B and C. Also, the plaster without reinforcement fibres had a lot of cracks and problems that cause plaster destroyed. The reinforcement fiber has greater effect on the drying shrinkage than sand.
The study recommends using the plaster with 30 °C drying temperature with a quantity of straw for improving the plaster materials to decrease the shrinkage and cracks.
References
Andrea V. K. and H. Harmuth (2008). Mechanisms to reduce cracking in interior plasters attached to cement bonded permanent shuttering panels. Const. and Build. Mat., 22(2):99-105.

ASHRAE (1997). ASHRAE Handbook, Fundamentals. N. Y. Am. Soc. Heat. and Refrig. and Air Cond. Eng., Inc.

ASTM D4943-(1995). Standard Test Method for Shrinkage Factors of Soils by the Wax Method. Annual Book of ASTM Standards, Vol. 04.08

Bai, Y., F. Darcy and P. A. M. Basheer (2005). Strength and drying shrinkage properties of concrete containing furnace bottom ash as fine aggregate. Const. and Build. Mat., 19(9):691-697.

Campbell, M. D. and R. S. P. Coutts (1980). Wood fibre-reinforced cement composites. J. of Mat. Sci., p:1962-1970.

DIN EN ISO, 12570 (2000).Waerme- und Feuchtetechnisches verhalten von Baustoffen und Bauprodukten–Bestimmung des Feuchtegehaltes durch Trocknen bei erhoehter Temperatur. p:1-4

Eve, S., M. Gomina, J. Hamel and G. Orange (2006). Investigation of the setting of polyamide fibre/latex-filled plaster composites. Const. and Build. Mat., 26(13):2541-2546.

Hashmi, F. (2008). Mud plasters and renders. http://www.appropedia.org/Mud_plasters_and_renders_(Practical_ Action_Brief):last update 1/10/ 2008.

Lerner, K. and K. Donahue (2003). Structural testing of plasters for straw bale construction. Ecobuild Network, www.ecobuildnetwork.org/pdfs/plaster_tests.pdf . Accessed September 14, 2005.

Omar, S., B. Al-Amoudi, O. T. Abiola and M. Maslehuddin (2006). Effect of super plasticizer on plastic shrinkage of plain and silica fume cement concretes. Const. and Build. Mat., 20(9):642-647.

Statistics
Article View: 144
PDF Download: 242