Ali, M., El-Nemr, K., Hamada, A., Abd-elhady, W. (2017). Effect of Gamma irradiation on mechanical behavior of EPDM rubber-recycled news print microfibers composites. test, 34(part1), 333-359. doi: 10.21608/jsrs.2018.14712
Magdy A. M. Ali; Khaled F. El-Nemr; Amina A. Hamada; Wafaa S. Abd-elhady. "Effect of Gamma irradiation on mechanical behavior of EPDM rubber-recycled news print microfibers composites". test, 34, part1, 2017, 333-359. doi: 10.21608/jsrs.2018.14712
Ali, M., El-Nemr, K., Hamada, A., Abd-elhady, W. (2017). 'Effect of Gamma irradiation on mechanical behavior of EPDM rubber-recycled news print microfibers composites', test, 34(part1), pp. 333-359. doi: 10.21608/jsrs.2018.14712
Ali, M., El-Nemr, K., Hamada, A., Abd-elhady, W. Effect of Gamma irradiation on mechanical behavior of EPDM rubber-recycled news print microfibers composites. test, 2017; 34(part1): 333-359. doi: 10.21608/jsrs.2018.14712

Effect of Gamma irradiation on mechanical behavior of EPDM rubber-recycled news print microfibers composites

Journal of Scientific Research in Science
Article 39, Volume 34, part1, September 2017, Pages 333-359    PDF (1.06 M)
Document Type: Original Article
DOI: 10.21608/jsrs.2018.14712
Authors
Magdy A. M. Ali1; Khaled F. El-Nemr1; Amina A. Hamada2; Wafaa S. Abd-elhady2
1Radiation Chemistry Department, National Center for Radiation Research and Technology, B.O. Box 29 Nasr City, Egyptian Atomic Energy Authority, Cairo Egypt
2AlAzhar University, Faculty of Sceince (Girls branch), Chemistry department
Abstract
The waste newsprint paperswere collected from local market  and submitted to chemical pulping in a kneader with 2M NaOH. The fiber after getting rid of water, treated again using 2M HCL solution for the same time period. Then the news print pulped microfibers (NPMF) batch obtained was mixed with Ethylene propylene diene monomer rubber (EPDM) on roll mill with differnet contents ranged from 5 to 50phr (part per hundred part of rubber). The prepared composites subjected to gamma irradiation at different doses from 20 up to 100kGy. The characterization of the microfibers carried out by different tools like scanning electron microscopy (SEM), X-ray diffraction (XRD),Forrier Transform Infrared spectra (FTIR) and Thermogravimetric analysis (TGA). The mechanical properties of prepared composites like tensile strength (Ts), Elongation at break (Eb%), tensile modulus(M100) , tensile toughness and crosslink density (Cd) were measured as a function of fiber contents and irrdaition dose. The results indicated the Ts was increased with increasing fiber content up to 10phr and incresed with increasing irradiation dose up to 40kGy, while Eb% decreased by fiber content and irradiation dose. M100 and Cd were incresed with invreasing fiber content up 50phr fiber and increased by irradiation dose up to 60kGy. The results concluded that toughness values of EPDM/ news print fiber composite reach maximum using 10phr fiber concentration and 60kGy irradiation dose.
 
Keywords
waste newsprint microfibers (NPMF)- EPDM/news print fiber composites Chemical repulping; Thermogravimetric analysis (TGA); X-ray difrraction (XRD); FTIR analysis– Mechanical properties