Effect Of Repeated Heat Pressing And Thermocycling On Micro Shear Bond Strength Of Polyetheretherketone (PEEK) To Resin Cement | ||
| Egyptian Dental Journal | ||
| Article 32, Volume 67, Issue 4, October 2021, Pages 3617-3627 PDF (1.41 M) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/edj.2021.90733.1752 | ||
| Authors | ||
| Ahmed Arafa1; Marwa Emam* 2 | ||
| 1Lecturer, Department of Fixed Prosthodontics, Faculty of Dentistry, Ain Shams University, Cairo, Egypt. | ||
| 2Lecturer, Department of Fixed Prosthodontics, Faculty of Dentistry, Beni-Suef University, Beni-Suef, Egypt | ||
| Abstract | ||
| Abstract: Purpose: to evaluate the effect of repeated heat pressing and thermocycling on micro-shear bond strength of PEEK to resin cement. Methods: A total of 30 PEEK specimens 10 mm x 10 mm x 2 mm were prepared and divided to three groups (n=10). Group I was pressed using new PEEK, Group II ; 50% new PEEK and 50% reprocessed PEEK, and Group III ; 100% reprocessed PEEK. Bonding surfaces were sandblasted and thin layer of bonding agent was applied and polymerized. Plastic tygon tubes with an inner diameter of 1 mm and a height of 1.5 mm were fixed on the sample and filled with dual polymerized self etch self adhesive resin cement and cured. Half the specimens in each group (n=5) underwent 5000 thermocycles (5‐55°C) before shear bond strength (µSBS) test. Two-way Analysis of Variance (ANOVA) studied the effect of PEEK condition, thermocycling and their interaction on mean micro-shear bond strength µSBS. Bonferroni’s post-hoc test was used for pair-wise comparisons when ANOVA test is significant. Results: The PEEK condition (regardless of thermocycling) had a statistically significant effect on mean µSBS (P-value = 0.001, Effect size = 0.455). Thermocycling (regardless of PEEK condition) also had a statistically significant effect on mean µSBS (P-value = 0.002, Effect size = 0.331). The interaction between two variables had no statistically significant effect on mean µSBS (P-value = 0.442, Effect size = 0.066). Conclusion: Both repeated heat pressing and thermocycling had a negative effect on micro-shear bond strength of resin cement to PEEK | ||
| Keywords | ||
| PEEK; heat pressing; reprocessing; thermocycling; shear bond strength | ||
|
Statistics Article View: 408 PDF Download: 405 |
||