Visualization the crystal structure, microstructure, magnetic performance and antimicrobial as well as anticancer activities of La0.5Sr0.5Mn0.9Ti0.1O3 nanopowders | ||
| Egyptian Journal of Chemistry | ||
| Article 3, Volume 65, Issue 12, December 2022, Pages 21-26 PDF (628.75 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/ejchem.2022.130541.5752 | ||
| Authors | ||
| Hesham Ahmed Tash* 1; Ali Omar Turky2; Ali Mostafa Hassan3; Hosni Anwar Gomaa3; Mohamed Mohamed Rashad4 | ||
| 1Chemistry, faculty of science, Al Azhar university, Nasr city, Egypt | ||
| 2Advanced Materials Institute Central Metallurgical R & D Institute (CMRDI), Helwan 87, Egypt | ||
| 3Chemistry Dep. Faculty of Science, Al-Azhar University, Nasr City 11884, Egypt | ||
| 4Electronic and magnetic materials lab., Advanced materials department, central metallurgical research and development institute | ||
| Abstract | ||
| Titanium substituted lanthanum strontium manganite LSMTO (La0.5Sr0.5Mn1-xTixO3, x= 0, 0.1) nanopowders were prepared via organic acid precursor using glycine-nitrate as fuel. The structural, microstructure, magnetic properties, anti-microbial activity as well as anti-cancer activity of La0.5Sr0.5Mn0.9Ti0.1O3 at different calcination temperatures from 800 to 1200oC for 2h were scrutinized. The ideal orthorhombic perovskite LSMTO with a space group Pbnm was proved at different synthesis conditions. However, substitution of Ti4+ ion instead of Mn4+ ion in LSMO annealed at different temperatures led to an increment of the crystallite size from 13.57 to 16.10 nm. The FT-IR spectrum elucidated that the bands around 600 cm-1 associated with Mn-O turn out broad imputed to Ti-O stretching modes. The morphology of the produced samples appeared as spherical groupings. The temperature dependence of magnetization confirms that Ti+4 ions were weakness the ferromagnetic (FM)-paramagnetic (PM) double exchange transition as the result of the break in the FM Mn3+–O–Mn4+ interactions. Molar magnetic susceptibility was notified to increase with the temperature. Subsequently, Curie temperature values were found to increase from 373 to 383 K with increasing the temperature, respectively. Eventually, LSMTO powders have cytotoxic effect on HepG-2 with IC50 value (105, 135 and 152 μg/ml) for LSMTO annealed at 800, 1000 and 1200 °C, respectively. | ||
| Keywords | ||
| Lanthanum strontium manganite; Fabrication; Characterization; Magnetic properties; Biomedical applications | ||
|