Effect of adding Tio2 nanoparticles on the properties of poly methyl methacrylate before and after thermocycling | ||
| Egyptian Dental Journal | ||
| Article 23, Volume 69, Issue 1 - Serial Number 4, January 2023, Pages 675-681 PDF (1.16 M) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/edj.2023.176776.2358 | ||
| Authors | ||
| Ali Bayiumy1; mohammad elsokkary* 2 | ||
| 1Lecturer of Prosthodontics, Faculty of Dentistry, Assiut University | ||
| 2Lecturer of Dental Materials, Faculty of Dentistry, Assiut University | ||
| Abstract | ||
| ABSTRACT: Objective: The aim of this study was to evaluate the effect of different concentrations of titanium dioxide nanoparticles on the mechanical properties of heat polymerized acrylic resin before and after thermocycling. The tested parameters were flexural strength and hardness Material and Methods: 120 specimens were prepared according to the specific dimension for each test (flexural strength and micro hardness) and distributed into - Before thermocycling (control, (TiO2) nanoparticles with concentration (0.1% and 0.2%) - After thermocycling (control, (TiO2) nanoparticles with concentration (0.1% and 0.2%) Thermal cycles were performed in a thermocycling machine consisted of 5000 cycles at 5°C and 55°C Results: Flexural strength and micro hardness were tested for both groups. The data was collected and statistically analyzed. Both Flexural strength and micro hardness were decreased by adding TiO2 nano particles concentrations. Conclusion: adding (TiO2) nanoparticles to methyl methacrylate adversely affects the flexural strength and micro hardness before and after thermocycling | ||
| Keywords | ||
| poly methyl methacrylate; TIO2 Nano particles; thermocycling; mechanical properties | ||
|