Hussein, M., Elsayed, E., Ibrahim, I. (2023). Preparation and characterization of cobalt ferrite CoFe2O4 thin films from alcoholic medium and their application restrictions. test, 3(3), 85-100. doi: 10.21608/ijmti.2023.170730.1067
Mostafa Rashad Hussein; Elsayed Mostafa Elsayed; Ibrahim ahmed Ibrahim. "Preparation and characterization of cobalt ferrite CoFe2O4 thin films from alcoholic medium and their application restrictions". test, 3, 3, 2023, 85-100. doi: 10.21608/ijmti.2023.170730.1067
Hussein, M., Elsayed, E., Ibrahim, I. (2023). 'Preparation and characterization of cobalt ferrite CoFe2O4 thin films from alcoholic medium and their application restrictions', test, 3(3), pp. 85-100. doi: 10.21608/ijmti.2023.170730.1067
Hussein, M., Elsayed, E., Ibrahim, I. Preparation and characterization of cobalt ferrite CoFe2O4 thin films from alcoholic medium and their application restrictions. test, 2023; 3(3): 85-100. doi: 10.21608/ijmti.2023.170730.1067

Preparation and characterization of cobalt ferrite CoFe2O4 thin films from alcoholic medium and their application restrictions

International Journal of Materials Technology and Innovation
Article 7, Volume 3, Issue 3, December 2023, Pages 85-100    PDF (1.48 M)
Document Type: Original Article
DOI: 10.21608/ijmti.2023.170730.1067
Authors
Mostafa Rashad Hussein* 1; Elsayed Mostafa Elsayed2; Ibrahim ahmed Ibrahim3
1Beni-Suef university
2Central metallurgical research and development institute.
3centeral metallurgical research and development institute.
Abstract
On various substrates, CoFe2O4 thin films were produced via an electrodeposition-anodization technique using a non-aqueous sulphate solution. At room temperature, the deposited alloy was electrochemically anodized (1M KOH) into the appropriate hydroxide. The cyclic voltammetric technique (CV) was used to investigate the electrodeposition of co-fe alloy to different substrate materials, to optimize the oxidation and reduction processes taking place on the surfaces of different electrodes. The Galvanostatic technique is also used to adjust the formation of the initial deposits. Also, the potentiodynamic polarization method was used to evaluate the corrosion performance of the ferrite on each substrate material and its stability.The crystal structure, crystallite size, microstructure, and magnetic properties of ferrite films were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometer (VSM) techniques.The obtained results revealed that cobalt ferrite nanoparticles deposited on Pt, SS and Cu substrates enhanced the magnetic and electrochemical properties. The corrosion rate results showed that CoFe2O4 thin film can be used safely in high acidic and alkaline atmospheres for Pt and SS substrates (high corrosion resistance), but not for Cu substrates at all pH values except pH = 9 (low corrosion resistance).
Keywords
Ferrites; Nanoparticles; Cyclic voltammetry; Corrosion rate; Polarization Curves