Carbon xerogel/Carbon Nanotubes Nanohybrid Doped with Ti for Removal of Methylene Blue Dye | ||
| Egyptian Journal of Chemistry | ||
| Article 9, Volume 62, Issue 12, December 2019, Pages 2277-2288 PDF (3.55 M) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/ejchem.2019.12870.1803 | ||
| Authors | ||
| Nady A Fathy* 1; Sahar Mohamed Elkhouly2; Reham Aboelenin2 | ||
| 1Physical Chemistry, Inorganic chemical industries division, National Research Centre, | ||
| 2National Research Centre | ||
| Abstract | ||
| A facile technology for decorating carbon xerogel (CX) with carbon nanotubes (CNTs) to prepare carbonaceous nanohybrid (CX-CNTs) was simultaneously implemented during carbonization of resorcinol-formaldehyde xerogel at 1123K meanwhile camphor as carbon nanotubes source is heated at 523K. Then the prepared CX-CNTs hybrid is doped with tetrabutyl orthotitanate as a titanium (Ti) precursor giving CX-CNTs-Ti nanohybrid used as an efficient photocatalyst. The morphology and textural properties of the samples were investigated using field-emission scanning electron microscope (FE-SEM), High resolution transmission electron microscopy (TEM) and N2 adsorption-desorption isotherm at 77K. The adsorption and photocatalytic properties of these samples toward methylene blue dye (MB) were performed. FE-SEM and TEM approved the formation of CNTs over the surface of CX and the developed nanohybrids have mesoporous structures. The adsorption efficiency of CX-CNTs and CX-CNTs-Ti samples was found to be 70 and 86.8% along 180 min, respectively. Under visible irradiation, the removal efficiency of CX-CNTs and CX-CNTs-Ti is enhanced to 90 and 99% at 60 min, respectively. Thus, CX-CNTs-Ti nanohybrid exhibited superior adsorptivity and photoactivity for removing MB dye as a result of the presence of Ti particles over CX-CNTs matrix. Doping CX-CNTs with Ti particles led to a decrease in the specific surface area and to enhance in both the total pore volume and amount of wider pores. Therefore, the reported CX-CNTs-Ti nanohybrid exhibits as an effective adsorbent and photocatalyst toward the removal of the MB dye from their aqueous solutions. | ||
| Keywords | ||
| Carbon xerogel; carbon nanotubes; Nanohybrid; Titanium; Adsorption; photocatalysis | ||
|