Assessment of Azolla Microphylla Plant Extract as an Environmentally Benign Corrosion Inhibitor for Low-Carbon Steel in Acidic Media | ||
| Egyptian Journal of Chemistry | ||
| Volume 67, Issue 10, October 2024, Pages 413-427 PDF (930.19 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/ejchem.2024.277352.9465 | ||
| Authors | ||
| Medhat M Kamel* 1; Mohamed A Ghanem2; Abdelaziz S Fouda3; Salah M Rashwan1; Osama M Abdelkader1; Nasser Y Mostafa4; Khaled M H Mohammed5 | ||
| 1[Kilo 4.5, Round road, Ismailia, Egypt] | ||
| 2Department of Chemistry, College of Science, King Saud University, Riyadh 11451, Saudi Arabia. | ||
| 3Faculty of Sci.,Mansoura Univ. | ||
| 4Al-daery | ||
| 5School of Chemistry, University of Southampton, Southampton SO17 1BJ, United Kingdom. | ||
| Abstract | ||
| In this study, Azolla Microphylla Extract (AME) appears as a potent corrosion inhibitor, effectively reducing the corrosion rate of low-carbon steel (CS) in a 1.0 M HCl solution. Comprehensive investigation methods, including weight loss (WL), potentiodynamic polarization (PP), electrochemical impedance spectroscopy (EIS), and electrochemical frequency modulation (EFM), were employed. The inhibition efficiency (IE) was evaluated across a range of extract concentrations (50-300 ppm) and temperatures (298-313 K). There is a good agreement between the results of electrochemical and WL methods. A remarkable IE of 98.1% was achieved at 313 K with 300 ppm of AME, displaying its effectiveness. At 298 K, the IE was 81.3%. Adsorption of AME on CS followed Langmuir isotherm and at temperatures of 308 K or lower the ΔGoads magnitudes were below –20 kJ mol-1, indicative of physical adsorption. However, at 313 K, ΔGoads exceeded –20 kJ mol-1, signaling a change to chemical adsorption. AME belongs to anodic inhibitors. The activation energy for the blank solution is 98.13 kJ mol-1, which decreased to 62.98 kJ mol-1 in the presence of 300 ppm of AME. Nyquist plots showed that AME inhibiting CS dissolution in HCl without altering the dissolution reaction mechanism. Attenuated total reflection infrared (ATR-IR) and scanning electron microscopy (SEM) inspections confirmed the adsorption of AME on CS. AME satisfies the general structural requirement of the corrosion inhibitor as it has O atoms in functional groups (O-H, C=C, and C=O) and an aromatic ring. The findings align well with other environmentally friendly inhibitors previously reported for CS corrosion. | ||
| Keywords | ||
| Azolla Microphylla; Plant extract; Corrosion; Inhibitor; Low-carbon steel; HCl media | ||
|