Effect of Simulated Intrapulpal Pressure on Microtensile Bond Strength of Self-adhesive Resin Composite to Dentin | ||
| Egyptian Dental Journal | ||
| Volume 70, Issue 3 - Serial Number 4, July 2024, Pages 2867-2876 PDF (333.26 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/edj.2024.282398.3004 | ||
| Author | ||
| Yasser Maher El-Bouhi* | ||
| Assistant professor - Department of Conservative and Restorative Dentistry - College of Dentistry - Umm Al-Qura University - Saudi Arabia. | ||
| Abstract | ||
| Background/Aim: This in vitro study aimed to evaluate the microtensile bond strength (µTBS) of a self-adhesive flowable resin composite (Vertise Flow) under simulated intrapulpal pressure IPP) and compare it to a conventional adhesive and flowable composite combination. Materials and Methods: Thirty human molars were used. IPP of 15 cm H2O was applied. Group I (control): Adeper Easy One + Z 250 (composite), Group II: Etching + Adeper Easy One + Z 250, Group III: Adeper Easy One + flowable composite + Z 250, Group IV: Etching + Adeper Easy One + flowable composite + Z 250, Group V: Vertise Flow + Z 250, and Group VI: Etching + Vertise Flow + Z 250. Data analysis employed one-way ANOVA with Tukey's post-hoc test for inter-group comparisons (at P < 0.05). Results: Etching the dentin prior to bonding with Adeper Easy One significantly increased µTBS to 25.12 MPa (S.D.: 5.78 MPa). Application of flowable composite resulted in a µTBS of 13.62 MPa (S.D. = 5.50 MPa), not statistically different. Group IV exhibited the highest mean µTBS (31.26 MPa, S.D. = 6.04 MPa). Group V showed the lowest mean µTBS (8.89 MPa, S.D. = 0.97 MPa). Etching before application of Vertise Flow in Group VI showed significant increased µTBS to 13.83 MPa (S.D. = 1.33 MPa) Conclusion: Dentin conditioning before application of Vetise Flow is necessary to produce a µTBS comparable to that of conventional approach of self-etch adhesive. | ||
| Keywords | ||
| Intrapulpal pressure; microtensile bond strength; self-etch; flowable composite; self-adhesive resin composite | ||
|