Wear, microhardness, water sorption, and solubility of conventional glass ionomer cement modified with precured nanofilled composite. | ||
| Advanced Dental Journal | ||
| Volume 6, Issue 4, October 2024, Pages 616-621 PDF (263.75 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/adjc.2023.201359.1281 | ||
| Authors | ||
| Diaa Asaad Elmwafy* 1; Amr Mohamed Abdelghany2 | ||
| 1Dental biomaterials, faculty of dentistry, Beni-Suef University | ||
| 2Spectroscopy Department, Physics Division National Research Center | ||
| Abstract | ||
| Aim: This study aimed to evaluate wear, microhardness, water sorption, and solubility of glassionomer cement modified with precured nanofilled composite. Subjects and Methods: Glass ionomer cement and nanofilled composite were used in this study. Glass ionomer cement was modified with precured nanofilled compositewith different concentrationsas follows: 0 wt%, 5 wt%, 10 wt%, 15wt% for the groups I, II, III, IV respectively. Wear, microhardness, water sorption, and solubility have been investigated. The data were statistically analyzed by one-way ANOVA and Tukey's HSD analysis at a significant factor of α = 0.05. Results: Regarding wear, water sorption, and solubility, the lowest value was for group IV, while the highest value was for group I.For, microhardness,the highest value was for group IV, while the lowest value was for group I. Conclusions:As the concentration of precured nanofilled composite powder increased in glass ionomer cement, the microhardness have been increased while wear, water sorption and solubility have been decreased. | ||
| Keywords | ||
| Glass ionomer cement modifed; composite; surface properties | ||
|