3D porous silicon (Nanorods Array, Nanosheets, and Nanoclusters) Production | ||
| Egyptian Journal of Chemistry | ||
| Article 10, Volume 63, Issue 4, April 2020, Pages 1269-1278 PDF (1.89 M) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/ejchem.2019.14613.1885 | ||
| Authors | ||
| Marwa M Nabil* 1; Kamal M Mahmoud2; Raghda Nomeir3; El-Maghraby El-Maghraby4; Hussien Motaweh5 | ||
| 1New Borg Elarab city- Alexandria | ||
| 2Department of Physics- Faculty of Science - Kafrelsheikh University | ||
| 3Department of Physics - Faculty of Science- Damanhour University | ||
| 4Department of Physics- Faculty of Science- Damanhour University | ||
| 5Department of Physics - Faculty of Science - Damanhour University | ||
| Abstract | ||
| In this research, using powder technology manufacturing is as a pioneering, low cost, a simple and safe method for the fabrication of nano-porous silicon (NPS-powder). It's attractive carriers for targeted in several research fields. It's prepared using a combination of alkali chemical etching process and ultra-sonication technique; through the utilization of commercial silicon powder; with high yield efficiency (81.43%). Several 3D-NPS-shapes (nanorods array, nanosheets, and nanoclusters) are fabricated. It's a mixture of microporous and mesoporous silicon powder {pore size (28-140 nm)}. The main factors which affect the production of NPS-powder are (KOHconc.), sonication time, separation process and drying velocity. | ||
| Keywords | ||
| microporous materials; chemical synthesis; X-Ray Diffraction | ||
|
Statistics Article View: 591 PDF Download: 436 |
||