SHEAR BOND STRENGTH OF UNIVERSAL-ADHESIVE TO DIFFERENT FIXED PROSTHODONTIC MATERIALS | ||
| Egyptian Dental Journal | ||
| Article 21, Volume 63, Issue 4 - October (Fixed Prosthodontics, Dental Materials, Conservative Dentistry & Endodontics), October 2017, Pages 3527-3534 PDF (1.5 M) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/edj.2017.76272 | ||
| Author | ||
| Diaaeldin Saad Awad | ||
| Lecturer of crown & bridge, Department of crown & bridge, Faculty of Dentistry, Suez Canal University. Ismailia, Egypt | ||
| Abstract | ||
| Objectives: To evaluate the shear bond strength (SBS) of Universal adhesive (Single Bond Universal SBU), that contain silane and MDP adhesive molecules, to different fixed prosthodontic materials (High-Leucite ceramics, Zirconia ceramics and base metal alloys). Methods: Twenty high-leucite based ceramics IPS Empress (Ivoclar) and twenty Ni-cr alloys Remanium-CSe(Dentaurum) specimens were constructed in discs of 5mm diameter and 3mm thickness. Twenty Zirconia based ceramics INcoris-TZI (Sirona) specimens were prepared of 19X15X3mm blocks. All specimens were embedded into acrylic resin blocks of 2x2X2cm. Composite discs 3mm in diameter Z-350(3M ESPE) were prepared and bonded to each material, divided into 2 groups according to the bonding procedures (N=10). High-Leucite ceramics etched with 5%HF acid then for Group1 composite discs were bonded with Single Bond2 SB2 and RelyX ultimate resin-cement RXU, after Silane Si application (Si+SB2+RXU), for Group 2 composite discs were bonded with Single Bond Universal adhesive and RelyX Ultimate without separate Silane application (SBU+RXU). Metal and zirconia specimens were air abraded 50µm AL2O3 then for Group 1; composite discs were bonded with Panavia cement only (Pa). For Group 2, composite discs were bonded with Single Bond Universal and RelyX Ultimate (SBU+RXU). All the specimens were thermo-cycled in water baths 5-55°C for 5000 cycles. The SBS was tested in a universal testing machine (Tira) using a chisel-edge blade. The results were statistically analyzed using Mann-Whitney test. Results: bThe mean (SBS±SD) in MPa were: In high leucite ceramics (23.1±2.5), (23.6± 1.9) for (Si+SB2+RUX) and (SBU+RUX) respectively. In Zirconia ceramics: (7.96± 3.1) and (16.8± 5.4) for (Pa) and (SBU+RXU) respectively. In Base metal alloys: (14.8±5.4) and (20.9±2.7) for (Pa) and (SBU+ RXU) respectively. Statistical analysis using Mann-Whitney test showed no significant difference for the high leucite and base metal groups (P>0.05) while there was significant difference for the zirconia groups (P<0.05). Conclusion: The Universal-adhesive SBU produced bond strength to high leucite-ceramics comparable to that of resin cement with separate Silane application. It produced higher bond strength to zirconia ceramics and base metal alloys in comparison to Panavia adhesive-resin cement. | ||
| Keywords | ||
| Universal adhesive; Shear bond strength; zirconia-ceramics; leucite-ceramics; base metal alloy | ||
|