Effect of different bonding techniques on the debonding characteristics of ceramic brackets | ||
| Egyptian Orthodontic Journal | ||
| Article 4, Volume 47, June 2015, June 2015, Pages 55-65 PDF (354.31 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/eos.2015.78727 | ||
| Authors | ||
| Moustafa Tageldin* ; Hanan Ismail; Mohamed Mowafy | ||
| Orthodontics department, Faculty of Dentistry, Alexandria University | ||
| Abstract | ||
| Objective: To evaluate and compare shear bond strength and debonding characteristics of ceramic brackets using different bonding techniques. Materials and Methods: Ninety six premolar teeth were randomly divided into six groups: 1) Transbond XT with 5 seconds etch, 2) Transbond XT with 15 seconds etch, 3) Transbond XT with Transbond Plus Self – Etching Primer, 4) Vertise Flow with 5 seconds etch, 5) Vertise Flow with 15 seconds etch, 6) Vertise Flow with Transbond Plus Self–Etching Primer. In each group 16 bracketed teeth with Inspire Ice bracket, 8 of which were debonded by universal testing machine to determine the shear bond strength. The other 8 ceramic brackets were removed with plastic debonding plier. All teeth were examined under a stereomicroscope, the adhesive remnant index and bracket fracture were assessed. Results: The mean SBS for group I to VI was (1.78 ± 0.78, 14.5 ± 5, 12.52 ± 3.69, 4.15 ± 2.35, 13.26 ± 4.46, 6.78 ± 3.51,) MPa respectively. Bracket fractures were noted in 10 out of 48 samples after debonding with plier. Groups II and V exhibited the higest SBS and the highest ratio of bracket fracture. Conclusion: Using 15 seconds etching with either Transbond XT or Vertise Flow gave acceptable SBS. Self-etching primer gave lower SBS but within the acceptable clinical range. Decreasing etching time to 5 seconds didn’t give clinically acceptable SBS | ||
|
Statistics Article View: 123 PDF Download: 198 |
||